The plasmonic resonance wavelength λres in ZnO doped with 3wt%Ga2O3 can be controlled over the range 1 – 4 μm by simple furnace annealing in flowing Ar. For each annealing temperature TA, the reflectance Rm and transmittance Tm are measured over a wavelength range, λ = 185 – 3200 nm, (energy range, E = 6.7 – 0.387 eV), and the reflectance coefficient R is calculated from Rm and Tm. The value of λres is then determined from a Drude-theory analysis of R vs E that yields fitting parameters nopt (optical carrier concentration), μopt (optical mobility), high-frequency dielectric constant ε∞, and thickness d, at each annealing temperature TA. The validity of this process is confirmed by comparison of ε∞ with literature values, and comparison of nopt and μopt with analogous quantities n and μH measured by the Hall-effect.
David C. Look, Kevin D. Leedy, Gordon J. Grzybowski, and Bruce B. Claflin, "Near-IR (1 – 4 μm) control of plasmonic resonance wavelength in Ga-doped ZnO," Proc. SPIE 10105, Oxide-based Materials and Devices VIII, 101050Q (Presented at SPIE OPTO: January 31, 2017; Published: 2 March 2017); https://doi.org/10.1117/12.2255763.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 12,000 conference presentations, including many plenary and keynote presentations.