Ga(AsBi) quantum well (QW) active regions are an alternate to dilute-nitride QWs for achieving lasers in the telecom wavelength regions (λ~1.3-1.55μm) on GaAs substrates. Ludewig et al first reported the successful operation of Ga(AsBi) single quantum well laser in 2013  with low threshold current densities, Jth=1.56kA/cm2 where (AlGa)As was used as a barrier material for low Bi-content QWs to improve the electron confinement in the conduction band and reduce thermally activated carrier leakage from the QW. We implement here the use of tensile-strained Ga(AsP) as a QW barrier material, providing carrier confinement as well as potential for strain-balancing. Laser structures employing a single GaAs0.976Bi0.024 quantum well (SQW) with either GaAs0.8P0.2, Al0.15Ga0.85As, or GaAs barrier materials were grown by MOVPE on a nominally singular (001) GaAs substrate Ridge waveguide lasers, 25μm-wide and 1mm-long ridge, were fabricated and characterized under pulsed current conditions. The threshold current densities for devices are 5.9kA/cm2 and 5.8kA/cm2 for GaAsP barriers and Al0.15Ga0.85As barriers respectively, with a lasing wavelength of 960nm. Devices with GaAs barriers only lased at higher currents for a short wavelength transition ~900nm. While threshold currents are relatively high, no post growth thermal annealing was performed on these laser materials. Thermal annealing studies will be presented indicating significant improvement in QW luminescence and reduction in Jth can be achieved after the post-growth in-situ annealing.
 Ludewig, P., Knaub, N., Hossain, N., Reinhard, S., Nattermann, L., Marko, I. P., and Volz, K. 2013. Appl. Phys. Lett., 102(24), 242115.
Honghyuk Kim, Yingxin Guan, Kamran Forghani, Thomas F. Kuech, and Luke J. Mawst, "Strain-compensated Ga(AsP)/Ga(AsBi)/Ga(AsP) quantum-well active-region lasers (Conference Presentation)," Proc. SPIE 10123, Novel In-Plane Semiconductor Lasers XVI, 1012304 (Presented at SPIE OPTO: January 30, 2017; Published: 20 April 2017); https://doi.org/10.1117/12.2251708.5398643850001.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 14,000 conference presentations, including many plenary and keynote presentations.