To research the attenuation performance of the AlGaN photocathode, three samples with same structures grown by metalorganic chemical vapor deposition (MOCVD) were activated with three different activation methods, which are Cs-only, Cs-O and Cs-O-Cs activation, respectively. The spectral responses and attenuated photocurrents of three AlGaN photocathodes were measured, the result shows that the Cs-O activated AlGaN photocathode have the lowest attenuation speed in the first few hours, the next are Cs-O-Cs and Cs-only activation, respectively. After the Cs-O-Cs activation sample has attenuated 90 min, its attenuation photocurrent curve is coincident with the Cs-O activation sample in the next measurement. The main factor which affects the photocurrent attenuation is Cs atom desorbed from the photocathodes surface.
Guanghui Hao, Junju Zhang, Yijun Zhang, Yafeng Qiu, and Yunsheng Qian, "Performance stability of reflection-mode AlGaN photocathode under different preparation methods," Proc. SPIE 10351, UV and Higher Energy Photonics: From Materials to Applications 2017, 1035107 (Presented at SPIE Nanoscience + Engineering: August 06, 2017; Published: 29 August 2017); https://doi.org/10.1117/12.2273319.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 12,000 conference presentations, including many plenary and keynote presentations.