Al2O3 has been an attractive gate dielectric for GaN power devices owing to its large conduction band offset with GaN (~2.13eV), relatively high dielectric constant (~9.0) and high breakdown electric field (~10 MV/cm). Due to exceptional control over film uniformity and deposition rate, atomic layer deposition (ALD) has been widely used for Al2O3 deposition. The major obstacle to ALD Al2O3 on GaN is its high interface-state density (Dit) caused by incomplete chemical bonds, native oxide layer and impurities at the Al2O3/GaN interface. Therefore, an appropriate surface pretreatment prior to deposition is essential for obtaining high-quality interface. In this study, we investigated the effect of TMA, H2O and Ar/N2 plasma pretreatment on Dit and border traps (Nbt). 5 cycles of TMA purge, 5 cycles of H2O purge and Ar/N2 plasma pretreatment were conducted on GaN prior to deposition of ALD Al2O3. Al2O3/GaN metaloxide-semiconductor capacitors (MOSCAPs) were fabricated for the characterization of Dit and Nbt using UV-assisted capacitance-voltage (C-V) technique. The results show that TMA and H2O pretreatment had trivial effects on interface engineering whereas Ar/N2 plasma pretreatment slightly reduced Dit and significantly reduced Nbt.
Jianyi Gao, Wenwen Li, Saptarshi Mandal, and Srabanti Chowdhury, "A study of the effect of surface pretreatment on atomic layer deposited Al2O3 interface with GaN," Proc. SPIE 10381, Wide Bandgap Power Devices and Applications II, 1038103 (Presented at SPIE Optical Engineering + Applications: August 08, 2017; Published: 23 August 2017); https://doi.org/10.1117/12.2279313.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 14,000 conference presentations, including many plenary and keynote presentations.