From Event: SPIE Optical Engineering + Applications, 2017
Piezoelectric adjustable optics are being developed for high throughput, high resolution, low mass Xray mirror assemblies. These optics require robust piezoelectric thin films and reproducible lithographic patterning on curved glass substrates. This work details the cleaning of Corning Eagle XG glass substrates for thin shell X-ray mirrors by a three stage acid and solvent cleaning procedure before a 0.02 μm Ti adhesion layer and a 0.1 μm Pt bottom electrode layer was deposited using DC magnetron sputtering. Piezoelectric Pb(Zr0.52Ti0.48)0.99Nb0.01O3 thin films with a thickness of 1.5 μm were then deposited by radio frequency magnetron sputtering in three 0.5 µm layers with intermittent annealing steps in a rapid thermal annealing furnace at 650°C for 60 seconds. Defects observed in the piezoelectric thin films were linked to residue remaining on the glass after cleaning. 112 piezoelectric cells and 100 μm wide conductive Pt traces were patterned using bilayer photolithography. The photoresist layers were deposited using spin coating at 2000 and 4000 RPM to achieve uniform 1 μm thick layers, resulting in reproducibly resolved features with limiting resolutions of approximately >25 μm. The resulting mirror pieces achieved a 100% yield, with average relative permittivity of 1270, dielectric loss 0.047, coercive field 30 kV/cm and remanent polarization of 20 μC/cm2 . While the defects observed in the films appeared to have not influence on the electrical properties, additional cleaning steps using DI water were proposed to further reduce their presence.
J. Walker, T. Liu, M. Tendulkar, D. Burrows, C. T. DeRoo, R. Allured, E. Hertz, V. Cotroneo, P. Reid, E. D. Schwartz, T. N. Jackson, and S. Trolier-McKinstry, "Design and fabrication of adjustable x-ray optics using piezoelectric thin films," Proc. SPIE 10399, Optics for EUV, X-Ray, and Gamma-Ray Astronomy VIII, 103991K (Presented at SPIE Optical Engineering + Applications: August 10, 2017; Published: 29 August 2017); https://doi.org/10.1117/12.2275351.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 14,000 conference presentations, including many plenary and keynote presentations.
Study of self-shadowing effect as a simple means to realize nanostructured thin films and layers with special attentions to birefringent obliquely deposited thin films and photo-luminescent porous silicon