Porous Nickel-Titanium shape memory alloys (NiTi-SMAs) have attracted much attention in biomedical applications due to their high range of pure elastic deformability (i.e., superelasticity) as well as their bone-level modulus of elasticity (E≈12-20 GPa). In recent years, Selective Laser Melting (SLM) has been used to produce complex NiTi components. The focus of this study is to investigate the superelasticity and compressive properties of SLM NiTi-SMAs. To this aim, several NiTi components with different level of porosities (32- 58%) were fabricated from Ni50.8Ti (at. %) powder via SLM PXM by Phenix/3D Systems, using optimum processing parameter (Laser power-P=250 W, scanning speed-v=1250mm/s, hatch spacing-h=120μm, layer thickness-t=30μm). To tailor the superelasticity behavior at body temperature, the samples were solution annealed and aged for 15 min at 350°C. Then, transformation temperatures (TTs), superelastic response, and cyclic behavior of NiTi samples were studied. As the porosity was increased, the irrecoverable strain was observed to be higher in the samples. At the first superelastic cycle, 3.5%, 3.5%, and 2.7% strain recovery were observed for the porosity levels of 32%, 45%, and 58%, respectively. However, after 10 cycles, the superelastic response of the samples was stabilized and full strain recovery was observed. Finally, the modulus of elasticity of dense SLM NiTi was decreased from 47 GPa to 9 GPa in the first cycle by adding 58% porosity.
Narges Shayesteh Moghaddam, Soheil Saedi, Amirhesam Amerinatanzi, Ahmadreza Jahadakbar, Ehsan Saghaian, Haluk Karaca, and Mohammad Elahinia, "Influence of SLM on compressive response of NiTi scaffolds," Proc. SPIE 10596, Behavior and Mechanics of Multifunctional Materials and Composites XII, 105960H (Presented at SPIE Smart Structures and Materials + Nondestructive Evaluation and Health Monitoring: March 06, 2018; Published: 22 March 2018); https://doi.org/10.1117/12.2305251.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 14,000 conference presentations, including many plenary and keynote presentations.
Study of self-shadowing effect as a simple means to realize nanostructured thin films and layers with special attentions to birefringent obliquely deposited thin films and photo-luminescent porous silicon