Lasing was observed from ZnO nanorods prepared by a simple method of chemical bath deposition (CBD) on ITOcoated glass substrates. The X-ray diffraction pattern showed a dominant peak for (002) plane typical for good crystalline quality of ZnO grown in the z-direction with a wurtzite structure. Continuous-wave photoluminescence (PL) spectra revealed a peak centered at 380 nm corresponding to the band gap of ZnO. Under pulsed optical pumping, lasing was observed above the nominal PL peak, initially for one mode at 384 nm. Two additional modes at 386 nm and 390 nm was observed when the pumping power is further increased. Threshold was achieved at 0.7 μJ which was 10 times smaller than that reported for powder-based random lasers. In addition, gain pinning was also observed for the dominant mode and the additional two modes appeared upon onset of this gain pining behavior.
M. N. Nordin, D. Priante, M. K. Shakfa, and W. Maryam, "Lasing from ZnO nanorods on ITO-coated substrates," Proc. SPIE 10682, Semiconductor Lasers and Laser Dynamics VIII, 106820O (Presented at SPIE Photonics Europe: April 25, 2018; Published: 9 May 2018); https://doi.org/10.1117/12.2307131.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 12,000 conference presentations, including many plenary and keynote presentations.