Scanning near-field PL spectroscopy was applied to study spatial variations of the emission spectra of AlGaN epilayers with AlN molar fractions between 0.3 and 0.7. Experiments were performed at 300 K with 100 nm spatial resolution. In general, photoluminescence spectra were found to be highly uniform with the peak energy deviation of 2 to 6 meV for different alloy compositions. In the 30% and 42% Al layers, a slightly lower Al content and a higher point defect concentration at the boundaries of growth domains were detected. These features were attributed to the higher mobility of Ga adatoms during growth. The inhomogeneous broadening beyond the random alloy distribution was found negligible for the 30% and 42% Al samples, and about 40–50 meV for the layers with a larger Al content.
S. Marcinkevičius, R. Jain, M. Shatalov, R. Gaska, and M. Shur, "Scanning near-field optical microscopy of AlGaN epitaxial layers," Proc. SPIE 9926, UV and Higher Energy Photonics: From Materials to Applications, 992605 (Presented at SPIE Nanoscience + Engineering: August 28, 2016; Published: 15 September 2016); https://doi.org/10.1117/12.2236999.
Conference Presentations are recordings of oral presentations given at SPIE conferences and published as part of the conference proceedings. They include the speaker's narration along with a video recording of the presentation slides and animations. Many conference presentations also include full-text papers. Search and browse our growing collection of more than 14,000 conference presentations, including many plenary and keynote presentations.
Study of self-shadowing effect as a simple means to realize nanostructured thin films and layers with special attentions to birefringent obliquely deposited thin films and photo-luminescent porous silicon