10 November 1986 OSEE As The Method Of Determining Of Defect Degree For A Fibre Preforms
Author Affiliations +
Proceedings Volume 0670, Optical Fibres and Their Applications IV; (1986) https://doi.org/10.1117/12.938976
Event: Optical Fibres and Their Applications, 1986, Warsaw, Poland
Abstract
OSEE decay curves for fibre preforms made from porous silicate glasses have been measured. Six glass types being final material of different processing staged were used as specimens. A point in which the decay curve practically coincides with the slowvarying term has been determined from the decay curve distribution. The parameter seems to be characteristic for given glass structural defect types. Exponent parameters have been also calculated which describe slow-varying part of the curve. Thus it seems that OSEE may be a good method for determination of imperfection degree of fibre preforms.
© (1986) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
St. Szarska, W. Magierski, "OSEE As The Method Of Determining Of Defect Degree For A Fibre Preforms", Proc. SPIE 0670, Optical Fibres and Their Applications IV, (10 November 1986); doi: 10.1117/12.938976; https://doi.org/10.1117/12.938976
PROCEEDINGS
5 PAGES


SHARE
RELATED CONTENT

Ultraviolet Content Of Lamps In Common Use
Proceedings of SPIE (February 19 1982)
Photosensitivity of rare-earth-doped glasses
Proceedings of SPIE (December 22 1993)
Silica Glass Fibers Modes Of Degradation And Thoughts...
Proceedings of SPIE (March 29 1984)
Printability and repair techniques for DUV photomasks
Proceedings of SPIE (February 12 1997)
SiO[sub]2[/sub] Film Grown On Glass In Aqueous Solution
Proceedings of SPIE (December 21 1989)

Back to Top