8 June 1988 The Effects Of Ionizing Radiation On Various Core/Clad Ratio Step Index Pure Silica Fibers
Author Affiliations +
Proceedings Volume 0867, Optical Devices in Adverse Environments; (1988) https://doi.org/10.1117/12.965057
Event: 1987 Symposium on the Technologies for Optoelectronics, 1987, Cannes, France
Under past radiation test results, it was observed that various combinations of coatings changed the radiation response characteristics of pure fused silica core step index fibers. The most radiation resistant fiber was that coated with a polyimide, which is cured with a high temperature. Based on this fact, additional testing was performed on polyimide coated fibers fabricated from different preform core/clad ratios. Our preliminary results indicated that the smaller the core/clad ratio the better the performance of the radiation response of the fiber. These results are fortuitous for space applications, since the polyimide coating is also a low-outgassing, wide-temperature range, small size fiber coating material. The test results indicate that the variations in radiation response may be due to a post-drawing anneal occurring during coating cure which minimizes drawing-induced defects.
© (1988) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
R A Greenwell, R A Greenwell, C E Barnes, C E Barnes, G W Nelson, G W Nelson, } "The Effects Of Ionizing Radiation On Various Core/Clad Ratio Step Index Pure Silica Fibers", Proc. SPIE 0867, Optical Devices in Adverse Environments, (8 June 1988); doi: 10.1117/12.965057; https://doi.org/10.1117/12.965057