9 November 2016 Fabrication and performance of In0.66Ga0.34As0.73P0.27/In0.89Ga0.11As0.23P0.77 mulltiple-quantum-well lasers
Author Affiliations +
Abstract
An In0.66Ga0.34As0.73P0.27/In0.89Ga0.11As0.23P0.77 quantum-well laser structure was grown on an InP substrate. The whole structure was grown by metalorganic chemical vapor deposition. The material quality was characterized by double crystal X-ray diffraction and room-temperature photoluminescence spectra. It shows that the active region’s optical properties are comparable to that InGaAs/InGaAsP quantum-well lasers. Meanwhile, we fabricated an InP-based InGaAsP/InGaAsP multiple quantum wells (MQWs) laser at 1.3 μm wavelength. Under quasi-continuous wave condition, a threshold current of 400 mA and the single side slope efficiency of 0.18 mW/mA are achieved for a broad area device with 100 μm-wide strip and 500 μm-long cavity at room-temperature. The wavelength of emission spectrum is 1305 nm. When the injection current is 700 mA, FWHM of the envelope is 3.6 nm.
© (2016) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Jia Chen, Jia Chen, Qi Wang, Qi Wang, Hao Liu, Hao Liu, Zhiming Li, Zhiming Li, Xiaomin Ren, Xiaomin Ren, } "Fabrication and performance of In0.66Ga0.34As0.73P0.27/In0.89Ga0.11As0.23P0.77 mulltiple-quantum-well lasers", Proc. SPIE 10017, Semiconductor Lasers and Applications VII, 100170L (9 November 2016); doi: 10.1117/12.2245987; https://doi.org/10.1117/12.2245987
PROCEEDINGS
5 PAGES


SHARE
Back to Top