4 November 2016 Gold nanoparticle-induced diameter reduction and enhanced Raman shift in self-rolled-up InGaAs/GaAs microtubes
Author Affiliations +
Abstract
Au nanoparticle-coated In0.2Ga0.8As/GaAs bilayers have been released from GaAs (100) substrate through selective wet etching of AlAs sacrificial layer, which provides a solution to implant metal nanoparticles (NPs) in the inner wall of self-rolled-up III-V semiconductor microtubes. Scanning electron microscope (SEM) reveals that the diameter of Au nanoparticle-decorated In0.2Ga0.8As/GaAs microtube is only 2.4μm, 300nm smaller than that of traditional counterparts. This phenomenon can be explained by that the surface tension of NPs and the intrinsic strain relaxation of In0.2Ga0.8As/GaAs bilayers both affect the rolling process. In order to understand the diameter reduction in Au-assistant microtubes, room temperature (RT) Raman measurements have been employed to study the strain effects reflected by the GaAs longitudinal optical (LO) phonon mode shifts when compared LO mode of microtubes with as-grown planar. The spectrum showed that there were about 10 wavenumbers and 2.6 wavenumbers red-shifts of GaAs LO for Au-assistant and non-Au-assistant structures, respectively, from which we calculated that about 2.56% and 0.66% strain change occurred. Au nanoparticle enhanced Raman shift clearly. According to this study, an approach to reduce the diameter of rolled-up microtubes was demonstrated, and this method may provide viable solution to fabricate nanotubes in the application for Lab-on-a-chip system.
© (2016) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Xiankun Wang, Xiankun Wang, Qi Wang, Qi Wang, Zhaoer Chai, Zhaoer Chai, Guoming Mao, Guoming Mao, Hao Liu, Hao Liu, Xiaomin Ren, Xiaomin Ren, } "Gold nanoparticle-induced diameter reduction and enhanced Raman shift in self-rolled-up InGaAs/GaAs microtubes", Proc. SPIE 10027, Nanophotonics and Micro/Nano Optics III, 100270N (4 November 2016); doi: 10.1117/12.2245993; https://doi.org/10.1117/12.2245993
PROCEEDINGS
6 PAGES


SHARE
Back to Top