Spray coated nanosilver functional layers

J. Krzemiński; J. Szałapak; L. Dybowska-Sarapuk; M. Jakubowska

doi:10.1117/12.2247682

Translator Disclaimer

28 September 2016 Spray coated nanosilver functional layers

J. Krzemiński, J. Szałapak, L. Dybowska-Sarapuk, M. Jakubowska

Author Affiliations +

Proceedings Volume 10031, Photonics Applications in Astronomy, Communications, Industry, and High-Energy Physics Experiments 2016; 1003104 (2016) https://doi.org/10.1117/12.2247682
Event: Photonics Applications in Astronomy, Communications, Industry, and High-Energy Physics Experiments 2016, 2016, Wilga, Poland

Abstract

Silver coatings are highly conductive functional layers. There are many different ways to product the silver coating but most of them need vacuum or high temperature. Spray coating is a technique that is free of this disadvantages – it doesn't need a cleanroom or high temperature. What's more the layer thickness is about 10 μm. In this article the spray coating process of silver nanolayer is described. Four different inks were tested and measured. The layer resistance was measured and show as a graph. After the layer resistance was measured the adhesion test was performed. The pull-off test was performed on testing machine with special self made module. To conclude the article include the test and measurements of spray coated nanosilver functional layers. The layers was examined for the current conductivity and adhesion force.

Citation Download Citation

J. Krzemiński, J. Szałapak, L. Dybowska-Sarapuk, and M. Jakubowska "Spray coated nanosilver functional layers", Proc. SPIE 10031, Photonics Applications in Astronomy, Communications, Industry, and High-Energy Physics Experiments 2016, 1003104 (28 September 2016); https://doi.org/10.1117/12.2247682

ACCESS THE FULL ARTICLE