24 February 2017 Zn-vacancy related defects in ZnO grown by pulsed laser deposition
Author Affiliations +
Proceedings Volume 10105, Oxide-based Materials and Devices VIII; 101050F (2017) https://doi.org/10.1117/12.2267186
Event: SPIE OPTO, 2017, San Francisco, California, United States
Abstract
Undoped and Ga-doped ZnO (002) films were grown c-sapphire using the pulsed laser deposition (PLD) method. Znvacancy related defects in the films were studied by different positron annihilation spectroscopy (PAS). These included Doppler broadening spectroscopy (DBS) employing a continuous monenergetic positron beam, and positron lifetime spectroscopy using a pulsed monoenergetic positron beam attached to an electron linear accelerator. Two kinds of Znvacancy related defects namely a monovacancy and a divacancy were identified in the films. In as-grown undoped samples grown with relatively low oxygen pressure P(O2)≤1.3 Pa, monovacancy is the dominant Zn-vacancy related defect. Annealing these samples at 900 oC induced Zn out-diffusion into the substrate and converted the monovacancy to divacancy. For the undoped samples grown with high P(O2)=5 Pa irrespective of the annealing temperature and the as-grown degenerate Ga-doped sample (n=1020 cm-3), divacancy is the dominant Zn-vacancy related defect. The clustering of vacancy will be discussed.
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
F. C. C. Ling, F. C. C. Ling, C. Q. Luo, C. Q. Luo, Z. L. Wang, Z. L. Wang, W. Anwand, W. Anwand, A. Wagner, A. Wagner, } "Zn-vacancy related defects in ZnO grown by pulsed laser deposition", Proc. SPIE 10105, Oxide-based Materials and Devices VIII, 101050F (24 February 2017); doi: 10.1117/12.2267186; https://doi.org/10.1117/12.2267186