20 February 2017 Luminescence of strained Ge on GeSn virtual substrate grown on Si (001)
Author Affiliations +
Proceedings Volume 10108, Silicon Photonics XII; 101080D (2017) https://doi.org/10.1117/12.2249564
Event: SPIE OPTO, 2017, San Francisco, California, United States
Abstract
To enlarge the tensile strain in Ge light emission diodes (s-Ge LED) we applied a GeSn virtual substrate (VS) on Si (001) with a Sn content of 4.5 %, to produce s-Ge LEDs. The LED stack was grown by molecular beam epitaxy. Electroluminescence investigations of the s-Ge LED show a major direct Ge peak and a minor peak at lower energy, which is formed by the GeSn-VS and the s-Ge indirect transition. The main peak of a 100 nm thick s-Ge LED is red-shifted as compared to the Ge peak of an unstrained reference Ge LED grown on Ge-VS. At a temperature of T = 80 K the increased tensile strain, produced by the GeSn-VS, causes a redshift of the direct Ge peak from 0.809 eV to 0.745 and 0.769 eV, namely for the s-Ge LED with a 100 and 200 nm thick active layer. At T = 300 K the direct Ge peak is shifted from 0.777 eV of the reference Ge LED to 0.725 eV (for 100 nm) and 0.743 eV (for 200 nm). The peak positions do not differ much between the 50 and 100 nm thick s-Ge LEDs. The intensities of the direct Ge peak increase with the s-Ge layer thickness. Moreover, the intensity of the 50 nm thick s-Ge sample is found to be larger than that of the 100 nm thick reference Ge LED.
Conference Presentation
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Bernhard Schwartz, Bernhard Schwartz, Michael Oehme, Michael Oehme, Roman Koerner, Roman Koerner, Stefan Bechler, Stefan Bechler, Jörg Schulze, Jörg Schulze, Martin Kittler, Martin Kittler, } "Luminescence of strained Ge on GeSn virtual substrate grown on Si (001)", Proc. SPIE 10108, Silicon Photonics XII, 101080D (20 February 2017); doi: 10.1117/12.2249564; https://doi.org/10.1117/12.2249564
PROCEEDINGS
7 PAGES + PRESENTATION

SHARE
RELATED CONTENT

Light from germanium tin heterostructures on silicon
Proceedings of SPIE (March 06 2013)
Si based GeSn light emitter mid infrared devices in...
Proceedings of SPIE (February 27 2015)
Monolithically integrated Ge CMOS laser
Proceedings of SPIE (February 19 2014)
Optical study of strain-free GeSn nanowires
Proceedings of SPIE (February 20 2017)
Single and multilayer Si Er structures for LED and...
Proceedings of SPIE (April 18 2006)

Back to Top