31 May 2017 Development of depth-graded W/Si multilayer mirrors for x-ray focusing telescope application
Author Affiliations +
Abstract
X-ray Timing and Polarization (XTP) telescope is proposed in China, by using the nested Wolter-I type optical system with large effective area, for the study of high energy physics at the region of 1-30 keV. High reflectance and low stress W/Si multilayers are demanded in the telescope to fulfill the spectral response and ensure the figure quality of the mirrors at the same time. A dedicated cylindrical deposition facility based on direct current magnetron sputtering technique was developed. Using this facility, W/Si multilayers fabricated under different base pressure and working pressure were tested to optimize the sputtering process. The microstructure and stress of W/Si multilayers with different d-spacing (d=2.0 nm-7.0 nm) and thickness ratio of W (ϒw=0.3-0.7) were studied. In order to obtain low stress multilayer mirrors, post-deposition annealing was applied on the multilayers and both the effects of temperature and annealing time were studied. Based on these works, a depth-graded W/Si multilayer was deposited on thin cylindrical mirror and the X-ray reflectivity was measured at Beijing Synchrotron Radiation Facility (BSRF).
Conference Presentation
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Runze Qi, Runze Qi, Qiushi Huang, Qiushi Huang, Yang Yang, Yang Yang, Zhong Zhang, Zhong Zhang, Zhanshan Wang, Zhanshan Wang, } "Development of depth-graded W/Si multilayer mirrors for x-ray focusing telescope application", Proc. SPIE 10235, EUV and X-ray Optics: Synergy between Laboratory and Space V, 102350G (31 May 2017); doi: 10.1117/12.2265752; https://doi.org/10.1117/12.2265752
PROCEEDINGS
8 PAGES + PRESENTATION

SHARE
RELATED CONTENT

Conceptual design of a fast soft x-ray stellar polarimeter
Proceedings of SPIE (November 06 1994)
W/C Mirror Deposition Optimization
Proceedings of SPIE (July 27 1989)
Multi-layer coating development for XEUS
Proceedings of SPIE (June 12 2006)

Back to Top