31 May 2017 Effect of ion beam etching on the surface roughness of bare and silicon covered beryllium
Author Affiliations +
Abstract
In the paper is studied the main aspects of using ion-beam etching for finish polishing. It is found that 400 eV is the optimal energy for neon ion etching ensuring slight surface roughness smoothing in the range of incidence angles of ± 40°. The deposition of 200 nm amorphous silicon films onto beryllium and their subsequent etching with the 800 eV argon ions improve the effective surface roughness integrated across the range of the spatial frequencies of 0.025-60 μm-1, from σeff=1.37 nm down to σeff=0.29 nm. The effectiveness of the smoothing technology for x-ray applications, confirmed by the results of the study the reflective properties of the Mo/Si mirrors deposited on the substrate. The reflectivity at a wavelength of 13.5 nm increased from 2% for the substrates with the surface roughness of σeff=2.3 nm (the roughness value corresponds to the as-prepared bulk Be substrates and is taken from the literature) up to 67.5% after the smoothing technology.
Conference Presentation
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
N. I. Chkhalo, N. I. Chkhalo, M. S. Mikhaylenko, M. S. Mikhaylenko, A. V. Mil'kov, A. V. Mil'kov, A. E. Pestov, A. E. Pestov, V. N. Polkovnikov, V. N. Polkovnikov, N. N. Salashchenko, N. N. Salashchenko, I. L. Strulya, I. L. Strulya, M. V. Zorina, M. V. Zorina, S. Yu. Zuev, S. Yu. Zuev, } "Effect of ion beam etching on the surface roughness of bare and silicon covered beryllium", Proc. SPIE 10235, EUV and X-ray Optics: Synergy between Laboratory and Space V, 102350M (31 May 2017); doi: 10.1117/12.2269312; https://doi.org/10.1117/12.2269312
PROCEEDINGS
10 PAGES + PRESENTATION

SHARE
RELATED CONTENT

CVD silicon carbide mirrors for EUV applications
Proceedings of SPIE (October 23 1995)
Development of new FIB technology for EUVL mask repair
Proceedings of SPIE (April 07 2011)
Correction of the EUV mirror substrate shape by ion beam
Proceedings of SPIE (April 29 2008)
Ion beam sputter deposition of x ray multilayer optics on...
Proceedings of SPIE (September 11 2006)
Ion beam sputtering of x-ray multilayer mirrors
Proceedings of SPIE (September 16 2008)

Back to Top