31 August 2017 Temperature dependency of mechanical properties for crystalline cellulose added to silicone elastomer
Author Affiliations +
Abstract
A chemical cross-linked transparent film was got by a silicon compound to crystalline cellulose. Temperature dependency for the elasticity modulus of a provided film was measured. The shear elastic modulus was obtained the value of 2 x 106 [Pa] at room temperature. The sample decreases in 190 [deg. C] for the elasticity modulus at the room temperature as 60%, but approximately 10% recover when temperature rises up to 200 [deg. C] or more.
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Takao Kameda, Takao Kameda, Naoto Sugino, Naoto Sugino, Satoshi Takei, Satoshi Takei, Makoto Hanabata, Makoto Hanabata, } "Temperature dependency of mechanical properties for crystalline cellulose added to silicone elastomer", Proc. SPIE 10354, Nanoengineering: Fabrication, Properties, Optics, and Devices XIV, 103541E (31 August 2017); doi: 10.1117/12.2273464; https://doi.org/10.1117/12.2273464
PROCEEDINGS
6 PAGES


SHARE
Back to Top