13 November 2017 Laser-induced modifications in fused silica up to damage initiation caused by multiple UV nanosecond pulses
Author Affiliations +
Abstract
Fatigue effects in fused silica have been largely studied in the past years, as this phenomenon is directly linked to the lifetime of high power photonic materials. Indeed, in the UV regime, we observe a decrease of the LIDT when the number of laser shots increases and this has been attributed to laser-induced material modifications. Under 266 nm laser irradiation, with nanosecond pulses of constant fluence, we observed that the photoluminescence is modified until damage occurs. High-OH fused silicas like Suprasil, “UV fused silica” or Herasil® show NBOHC (Non-Bridging Oxygen Hole Center) luminescence at 664 nm (1.87 eV) whereas low-OH fused silica like Infrasil shows ODC (Oxygen- Deficient Center) luminescence at 404 nm (3.07 eV). We found that the laser-induced density of NBOHCs increased until bulk damage occurred while the ODC’s density decreased. We propose a new representation of the experimental Son- 1 breakdown data which allows predicting the occurrence of material breakdown consuming fewer sample surface and saving time compared to the classic representation Nd (Number of shots before damage) versus F (Fluence). The link between LIF and the modifications leading to breakdown is however modified if a break is used during the irradiation.
© (2017) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Alexandre Beaudier, Alexandre Beaudier, Frank R. Wagner, Frank R. Wagner, Jean-Yves Natoli, Jean-Yves Natoli, } "Laser-induced modifications in fused silica up to damage initiation caused by multiple UV nanosecond pulses", Proc. SPIE 10447, Laser-Induced Damage in Optical Materials 2017, 104470B (13 November 2017); doi: 10.1117/12.2280529; https://doi.org/10.1117/12.2280529
PROCEEDINGS
7 PAGES


SHARE
Back to Top