23 February 2018 Fe:Zn0.6Mn0.4Se laser generation at 5.0 – 5.8-μm in the temperature range of 78 – 300 K
Author Affiliations +
Abstract
The goal of this study was the investigation of temperature-dependent spectroscopic and laser properties of novel Fe:ZnMnSe crystal with high manganese (Mn) content of 0.4. The fluorescence spectrum at 78 K is broad covering the region from 4000 to 5500 nm. In comparison with a Fe:ZnSe crystal, the fluorescence maximum shift of ~600 nm towards the mid-IR region can be observed. With the increasing temperature, the fluorescence spectrum is getting generally broader together with the maximum shift towards the mid-IR spectral region. The central laser oscillation wavelengths were increasing with temperature from 5450 nm at 78 K up to 5800 nm at 300 K. The output energies were decreasing from 2 mJ at 78 K to 0.1 mJ at 300 K. To our best knowledge, these are the longest oscillation wavelengths generated using a ZnSe-based crystal under Er:YAG laser excitation.
© (2018) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
H. Jelínková, H. Jelínková, M. E. Doroshenko, M. E. Doroshenko, V. V. Osiko, V. V. Osiko, M. Jelínek, M. Jelínek, D. Vyhlídal, D. Vyhlídal, J. Šulc, J. Šulc, M. Němec, M. Němec, N. O. Kovalenko, N. O. Kovalenko, A. S. Gerasimenko, A. S. Gerasimenko, } "Fe:Zn0.6Mn0.4Se laser generation at 5.0 – 5.8-μm in the temperature range of 78 – 300 K", Proc. SPIE 10511, Solid State Lasers XXVII: Technology and Devices, 1051128 (23 February 2018); doi: 10.1117/12.2289678; https://doi.org/10.1117/12.2289678
PROCEEDINGS
7 PAGES


SHARE
Back to Top