14 May 2018 Tuning of temperature coefficient of resistivity in poly-crystalline VO2 via chemical doping
Author Affiliations +
Abstract
We explored the effect of Cr dopant on the transport behaviors of polycrystalline VO2 thin films in order to suppress the sharp metal-insulator transition, and tune the temperature coefficient of resistivity (TCR) value. A reactive bias target ion beam deposition was used for combinational sputtering to Cr doped VO2 thin films (~100 nm). The addition of Cr led a structural change in the semiconducting phase of VO2. With the Cr content >7 at. %, the sharp metal-semiconductor transition and the hysteresis loop was suppressed in thin film VO2. A further increase of Cr content reduced the TCR. Separately the effect of the oxygen flow rate was investigated to modulate the TCR and the resistivity value of Cr doped VO2. We demonstrated the resistivity of Cr doped VO2 was modulated by 2 orders of magnitude with a very small change in the oxygen flow rate. We obtained TCR of ~ 4.5 %/K in Cr doped VO2 grown on single crystal sapphire substrate near room temperature.
Conference Presentation
© (2018) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Salinporn Kittiwatanakul, Salinporn Kittiwatanakul, Noah Sauber, Noah Sauber, Mike Cyberey, Mike Cyberey, Arthur Lichtenberger, Arthur Lichtenberger, Robert Weikle, Robert Weikle, Jiwei Lu, Jiwei Lu, } "Tuning of temperature coefficient of resistivity in poly-crystalline VO2 via chemical doping", Proc. SPIE 10656, Image Sensing Technologies: Materials, Devices, Systems, and Applications V, 106560A (14 May 2018); doi: 10.1117/12.2304303; https://doi.org/10.1117/12.2304303
PROCEEDINGS
6 PAGES + PRESENTATION

SHARE
RELATED CONTENT

Fully automated inline sputtering for optical coatings
Proceedings of SPIE (February 25 2004)
The study of the birefringence as MoSi based materials for...
Proceedings of SPIE (September 23 2009)
SiC: filter for extreme ultraviolet
Proceedings of SPIE (September 16 1994)
Sputtering of silicate glasses
Proceedings of SPIE (November 01 1991)

Back to Top