6 June 1995 High-performance linear arrays of YBa2Cu3O7 superconducting infrared microbolometers on silicon
Author Affiliations +
Abstract
Single detectors and linear arrays of microbolometers utilizing the superconducting transition edge of YBa2Cu3O7 have been fabricated by micromachining on silicon wafers. A D* of 8 +/- 2 X 109 cm Hz1/2/watt has been measured on a single detector. This is the highest D* reported on any superconducting microbolometer operating at temperatures higher than about 70 K. The NEP of this device was 1.5 X 10-12 watts/HzHLF at 2 Hz, at a temperature of 80.7 K. The thermal time constant was 105 msec, and the detector area was 140 micrometers X 105 micrometers . The use of batch silicon processing makes fabrication of linear arrays of these detectors relatively straightforward. The measured responsivity of detectors in one such array varied by less than 20% over the 6 mm length of the 64-element linear array. This measurement shows that good uniformity can be achieved at a single operating temperature in a superconductor microbolometer array, even when the superconducting resistive transition is a sharp function of temperature. The thermal detection mechanism of these devices gives them broadband response. This makes them especially useful at long wavelengths (e.g. (lambda) > 20 micrometers ), where they provide very high sensitivity at relatively high operating temperatures.
© (1995) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Burgess R. Johnson, Burgess R. Johnson, Marc C. Foote, Marc C. Foote, Holly A. Marsh, Holly A. Marsh, } "High-performance linear arrays of YBa2Cu3O7 superconducting infrared microbolometers on silicon", Proc. SPIE 2475, Infrared Detectors and Instrumentation for Astronomy, (6 June 1995); doi: 10.1117/12.211293; https://doi.org/10.1117/12.211293
PROCEEDINGS
6 PAGES


SHARE
Back to Top