13 May 1997 Photoinduced processes in silicate glasses exposed to IR femtosecond pulses
Author Affiliations +
The optical properties variation in silicate glasses after exposure to high-power femtosecond laser radiation at 0.85 micrometers have been studied. The laser spectral line broadening leading to the supercontinuum generation in visible and UV spectral regions was observed in all studied glasses. Color center generation and intrinsic luminescence were found in boro- and alkali-silicate glasses. It is believed that these processes result from linear and/or two-photon absorption of the short-wavelength part of this supercontinuum which causes glass matrix ionization. No color center absorption in the visible region was observed in fused silica at irradiances up to the laser damage threshold. It was concluded that there is no significant ionization of fused silica under exposure to IR femtosecond laser pulses with irradiance below laser induced damage threshold.
© (1997) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Oleg M. Efimov, Oleg M. Efimov, Kai M. Gabel, Kai M. Gabel, Serge V. Garnov, Serge V. Garnov, Leonid B. Glebov, Leonid B. Glebov, Steve E. Grantham, Steve E. Grantham, Martin C. Richardson, Martin C. Richardson, M. J. Soileau, M. J. Soileau, } "Photoinduced processes in silicate glasses exposed to IR femtosecond pulses", Proc. SPIE 2966, Laser-Induced Damage in Optical Materials: 1996, (13 May 1997); doi: 10.1117/12.274231; https://doi.org/10.1117/12.274231

Back to Top