18 August 1997 Modulation and scanning-frequency effects in laser cladding process
Author Affiliations +
Proceedings Volume 3097, Lasers in Material Processing; (1997) https://doi.org/10.1117/12.281112
Event: Lasers and Optics in Manufacturing III, 1997, Munich, Germany
Abstract
In the present work, the results of laser cladding by galvano scanning and modulated beam using the CO2 and Nd-YAG lasers are presented. The results are compared with the stationary beam. It is realized that the scanning frequency as well as the modulation effects were found to have significant effects on solidification and microstructural development process. The results indicate that the dendrite structure shall be fine at higher frequency or low duty modulation condition, compared to the coarse structure at lower frequency or high duty modulation condition. A shallow bead width as wide as 10 mm was obtained in a single pass. Macro- and micro- crossection, EPMA and microhardness profile have been employed to characterize the cladding. The results are correlated with the cladding quality. Microstructure, hardness, dilution etc. are discussed as a function of the processing parameter. Because of the high solidification rate a fine dendrite structure is developed in the cladding zone. A few of the actual results and EPMA analysis of the laser cladding of stellite 6 on 12 Cr-Ni turbine blade as shown in the figure are presented.
© (1997) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Yash P. Kathuria "Modulation and scanning-frequency effects in laser cladding process", Proc. SPIE 3097, Lasers in Material Processing, (18 August 1997); https://doi.org/10.1117/12.281112
PROCEEDINGS
8 PAGES


SHARE
Advertisement
Advertisement
RELATED CONTENT

Laser polishing
Proceedings of SPIE (February 15 2012)
Innovative Schemes For Single Transverse-Mode Lasers
Proceedings of SPIE (July 10 1987)
Self-Q-switched asymmetry of flat-flat-cavity solid laser
Proceedings of SPIE (September 05 2002)
Surface remelting of ductile iron with a high power pulsed...
Proceedings of SPIE (September 07 1994)
Cross-section modeling of pulsed Nd:YAG laser cladding
Proceedings of SPIE (November 04 1994)

Back to Top