A series of optically transparent SiO2: polydimethylsiloxane (PDMS) polyceram monoliths have been synthesized by two-step acid/base sol-gel processes. Two different processing routes are discussed and compared; one synthetic route (Route 1) utilizes lower water content, shorter reflux times, and faster drying conditions compared to the other synthetic route (Route 2). The Route 1 polycerams were all essentially non-porous at all PDMS contents examined (20 - 80 volume % PDMS). In contrast, the porosity of the Route 2 polycerams varied dramatically as a function of PDMS content. The surface area and pore volume for a 0% PDMS Route 2 polyceram were 573 m2/gm and 0.59 cm3/gm, respectively; the surface area and pore volume decreased with increasing PDMS content. The amount of porosity within the polycerams is proposed to be controlled by the relative rates of condensation and evaporation during processing and by the amount of PDMS trapped in the pores. This idea is supported by the differences in the drying behavior with processing and by the structural information obtained by magic angle spinning solid-state 29Si NMR of the polyceram monoliths. Quantitative evaluation of the 29Si NMR and porosity data are utilized to formulate structural models of these polycerams. The structural models are then specifically used to describe the effect of porosity on the photostabilization of a laser dye doped within these polyceram monoliths.
Tayyab I. Suratwala,Kevin Davidson,Zack Gardlund, andDonald R. Uhlmann
"Control of porosity in SiO2:PDMS polycerams through variations in sol-gel processing and polymer content", Proc. SPIE 3136, Sol-Gel Optics IV, (2 October 1997); https://doi.org/10.1117/12.284130
ACCESS THE FULL ARTICLE
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.
The alert did not successfully save. Please try again later.
Tayyab I. Suratwala, Kevin Davidson, Zack Gardlund, Donald R. Uhlmann, "Control of porosity in SiO2:PDMS polycerams through variations in sol-gel processing and polymer content," Proc. SPIE 3136, Sol-Gel Optics IV, (2 October 1997); https://doi.org/10.1117/12.284130