8 September 1998 Thin film front protection of CMOS wafers against KOH
Author Affiliations +
Proceedings Volume 3514, Micromachined Devices and Components IV; (1998); doi: 10.1117/12.323880
Event: Micromachining and Microfabrication, 1998, Santa Clara, CA, United States
KOH based silicon bulk micromachining of fully processed CMOS wafers is still a challenge since KOH heavily attacks the aluminum metallizations. At present, the protection of the front of such wafers is still accomplished using mechanical fixtures. These fixtures prevent batch processing. This paper reports a novel protection scheme for the front side of fully processed CMOS wafers against KOH solutions. Since no mechanical fixture is required the new scheme allows batch micromachining. The protection method uses standard CMOS equipment and materials only and is therefore fully CMOS compatible. Different protection schemes based on silicon nitride and oxynitride PECVD thin films are investigated. With a 4 hour etch in a 27 weight-% (wt%) KOH solution at 95 degree(s)C, membranes consisting of the CMOS dielectrics were successfully produced. After KOH etching the protection layers are removed in an reactive ion etcher (RIE). Two aspects of the protection schemes were investigated in detail. First, we analyzed the influence of the stress in the nitride layer on the fabrication yield. With an optimized recipe with a compressive stress of -150 MPa, more than 99% of all contact pads remain intact after the KOH etching. Secondly, potassium contamination of the RIE etcher is negligible if the wafers undergo an RCA cleaning procedure. Secondary ion mass spectroscopy showed that the total alkaline contaminations in thermal oxide, silicon, silicon nitride and silicon oxynitride after the RCA cleaning are not higher than those in reference samples not exposed to the KOH solution.
© (1998) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Ulrich Munch, Niklaus Schneeberger, Oliver Paul, Henry Baltes, Elko Doering, "Thin film front protection of CMOS wafers against KOH", Proc. SPIE 3514, Micromachined Devices and Components IV, (8 September 1998); doi: 10.1117/12.323880; https://doi.org/10.1117/12.323880


Patterning in the era of atomic scale fidelity
Proceedings of SPIE (March 17 2015)
Etch tailoring through flexible end-point detection
Proceedings of SPIE (March 01 1991)
Role of RIE in microchip bond pad corrosion
Proceedings of SPIE (September 12 1996)
Bonding and deep RIE a powerful combination for high...
Proceedings of SPIE (January 22 2005)

Back to Top