28 January 1999 Corrosion quantification by different nondestructive inspection methods
Author Affiliations +
Abstract
Boeing investigated corrosion effects on crack growth rates under a USAF contract with Tinker AFB in an engineering assignment performed by the Boeing Wichita. Sixty-eight crack growth specimens were notched, corroded, and fatigue test to determine crack growth rates. After salt spray exposure and crack growth testing the specimens were nondestructively inspected (NDI) by five different NDI methods to determine the amount of material lost. The NDI methods were chosen to represent different methods that could detect the presence of corrosion and digitize the data for analysis later to determine percent material lost. The NDI methods evaluated were computed tomography, pulse-echo ultrasonic c-scan, eddy current c-scan, thermography and digital radiography. Microscopy cross sectioning was also performed to visually document the corrosion damage. This data was used to compare the effectiveness of the NDI methods for detecting and quantifying corrosion damage and was used in the reanalysis of pre-corroded crack growth data. The results of NDI portion of this study are presented.
© (1999) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Paul S. Rutherford and Joe J. Luzar "Corrosion quantification by different nondestructive inspection methods", Proc. SPIE 3586, Nondestructive Evaluation of Aging Aircraft, Airports, and Aerospace Hardware III, (28 January 1999); https://doi.org/10.1117/12.339881
PROCEEDINGS
12 PAGES


SHARE
Advertisement
Advertisement
Back to Top