15 July 1999 Crystallinities and light-emitting properties of nanostructured SiGe alloy prepared by pulsed laser ablation in inert background gases
Author Affiliations +
Abstract
For studying the material properties of nanostructured group IV materials, we have developed a pulsed laser ablation method into inert background gases. SiGe alloy nanocrystallites have possibility of novel band structure engineering by controlling not only compositions but also particle sizes. An ArF excimer laser was focused onto the surface of the powder-sintered SixGe1-x target. During the laser ablation, He gas was introduced into a vacuum chamber and was maintained at a constant pressure. Size distribution of the SixGe1-x ultrafine particles decreases with decreasing composition x under fixed conditions of deposition such as background gas pressure. Raman scattering spectra of the deposited SiGe ultrafine particles show three peaks ascribed to mixed crystalline SiGe after annealing, and the linewidths of the peaks broaden due to the reduced size of the crystallites. The frequencies and intensities of the peaks depend on the composition x. Visible PL spectra have broad peaks from 2.25 eV to 2.10 eV, at room temperature. The peak positions show blue shifts with increasing x. Electroluminescent diodes with the Si0.8Ge0.2 nanocrystallite active region were fabricated, and emit visible high peaked at around 1.8 3V, at room temperature.
© (1999) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Takehito Yoshida, Yuka Yamada, Nobuyasu Suzuki, Toshiharu Makino, Takaaki Orii, Kouichi Murakami, David B. Geohegan, Douglas H. Lowndes, Michael J. Aziz, "Crystallinities and light-emitting properties of nanostructured SiGe alloy prepared by pulsed laser ablation in inert background gases", Proc. SPIE 3618, Laser Applications in Microelectronic and Optoelectronic Manufacturing IV, (15 July 1999); doi: 10.1117/12.352722; https://doi.org/10.1117/12.352722
PROCEEDINGS
8 PAGES


SHARE
RELATED CONTENT

Light Scattering From Ultrathin Si And Ge Layers
Proceedings of SPIE (July 05 1989)
Semiconducting silicide photonic devices
Proceedings of SPIE (September 10 2007)
Green photoluminescence from nc-Ge particles
Proceedings of SPIE (September 30 1996)

Back to Top