30 December 1999 High-transmission PSM inspection sensitivity
Author Affiliations +
Manufacturing of reticles, which combine both OPC and PSM, is becoming more and more challenge. Materials cost is high, several accurate writing processes are needed and repair is almost impossible. This makes inspection a critical and very complicated process. This study describes an inspection of a test vehicle consisting of 55 cells targeted for sub- wavelength design rule technology. This study describes an inspection of the 55 cells test plate targeted for 0.17 micrometer design rule technology. The plate is written on a MoSi layer with 18% transmission for 248 nm lithography. The MoSi has higher transmittance in I-line and G-line that reduces the contrast between the MoSi and the glass (relative to the usual contrast in binary plates). The technique for inspection by Applied Materials RT8000ES 436nm die-to-database is described. The technique is based on expansion of the reduced dynamic range of gray level that results from the lower contracts, re-gaining the inspection capability. This paper reviews the results of G-line versus I-line inspection of high transmission PSM and describes the method of the sensitivity verification including CD defects analysis.
© (1999) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Chunhung Wu, Chunhung Wu, David Wang, David Wang, Chien-Ming Wang, Chien-Ming Wang, Li-Jui Chen, Li-Jui Chen, Shuo-Yen Chou, Shuo-Yen Chou, Clare Wu, Clare Wu, Nathan Schumann, Nathan Schumann, Reuven Falah, Reuven Falah, Wolfgang Staud, Wolfgang Staud, } "High-transmission PSM inspection sensitivity", Proc. SPIE 3873, 19th Annual Symposium on Photomask Technology, (30 December 1999); doi: 10.1117/12.373307; https://doi.org/10.1117/12.373307


2013 mask industry survey
Proceedings of SPIE (September 19 2013)
Requirements of attenuated PSM for 0.18-um gate patterns
Proceedings of SPIE (August 31 1998)
Attenuated phase-shifting mask in ArF lithography
Proceedings of SPIE (August 24 1999)

Back to Top