3 March 2000 Refined statistical measurements of laser damage
Author Affiliations +
Abstract
By direct observation of individual damage sites on the surface of a component, the local fluence of every damage site was obtained. This more accurate measurement was used to evaluate the real defect density at each fluence. These results were compared to some others, calculated from damage fluences distributions, obtained from R/1 test. Results presented here concern fused silica with a regular polish. The experimental set up used for this work was equipped with a 3.7ns Nd:YAG pulsed laser at 1 (omega) . The laser beam diameter was 1.1mm and the angle of incidence was close to 0 degrees.
© (2000) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Patricia Volto, A. Roussel, C. Cordillot, D. Bernardino, Herve Bercegol, "Refined statistical measurements of laser damage", Proc. SPIE 3902, Laser-Induced Damage in Optical Materials: 1999, (3 March 2000); doi: 10.1117/12.379316; https://doi.org/10.1117/12.379316
PROCEEDINGS
7 PAGES


SHARE
Back to Top