24 March 2000 Calcium solubility of dental enamel following Er, Cr:YSGG laser irradiation
Author Affiliations +
Proceedings Volume 3910, Lasers in Dentistry VI; (2000); doi: 10.1117/12.380844
Event: BiOS 2000 The International Symposium on Biomedical Optics, 2000, San Jose, CA, United States
Abstract
Ever since the laser was introduced in dental medicine, there has been a constant discussion about its use in caries prevention. Various studies have already illustrated the possible uses of CO2 and argon lasers in this field of dentistry. The aim of the present study was to examine the Er,Cr:YSGG laser with regard to potential in reducing the acid solubility of dental enamel. Thirty freshly extracted bovine incisor teeth were prepared for this purpose. The crowns of the teeth were covered with hard wax, leaving a standardized test area free. The test specimens were then divided into three groups. The test area was uniformly irradiated with 2.7 J/cm2 in the first test group and 6.5 J/cm2 in the second test group. The third test group was left untreated (control group). Demineralization of the teeth was performed over a period of 24 hours in acetate buffer solution (0.1 mol/l) with a pH value of 4.5 and a temperature of 37 degrees Celsius. The calcium content of the solution was subsequently determined by flame photometry. The results confirm a significantly lower calcium content in the test group exposed to radiation of 6.5 J/cm2 (p less than 0.025). Dental enamel seems to have increased acid resistance following irradiation with the Er,Cr:YSGG laser.
© (2000) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Christian Apel, Hans-Georg Graeber, Norbert Gutknecht, "Calcium solubility of dental enamel following Er, Cr:YSGG laser irradiation", Proc. SPIE 3910, Lasers in Dentistry VI, (24 March 2000); doi: 10.1117/12.380844; https://doi.org/10.1117/12.380844