6 September 2000 Temperature variations of dielectric properties for single-domain/single-crystal thin films of Pb-Ti-O families
Author Affiliations +
Abstract
Temperature variations of dielectric and/or ferroelectric properties were evaluated for the continuous single c-domain/single crystal thin films of Pb-Ti-O families, PbTiO3 (PT) and Pb0.8La0.2TiO0.95 [PLT(20)]. The thin films of Pb-Ti- O families, 100 to 300 nm in film thickness, were epitaxially grown on the miscut (001)SrTiO3) (ST)substrates by using rf-magnetron sputtering. The sputtered PT and PLT(20) thin films were tetragonally deformed, but the thin films were tightly bonded to the substrates. These thin films did not show the temperature anomaly in the lattice parameter unlikely to the bulk ferroelectric materials. The dielectric properties of the Pb-Ti-O thin films were evaluated in a Au/Pb-Ti-O/SRO/ST heterostructure with evaporated Au top electrodes and sputtered SRO (SrRuO3) base electrodes. The dielectric measurements showed the hysteresis feature at the heating up and cooling down stage probably due to the temperature change of their interfacial structure. The temperature-dielectric properties of the PT thin films showed the diffused peak at about 520 degree(s)C - 525 degree(s)C, which would corresponded the Curie temperature. The P/E hysteresis curves of the PT thin films showed zero polarization at 525 degree(s)C. The similar diffused temperature anomaly was also observed for the PLT(20) thin films.
© (2000) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Goh Asayama, Goh Asayama, Ryuta Ai, Ryuta Ai, Kiyotaka Wasa, Kiyotaka Wasa, } "Temperature variations of dielectric properties for single-domain/single-crystal thin films of Pb-Ti-O families", Proc. SPIE 4058, Superconducting and Related Oxides: Physics and Nanoengineering IV, (6 September 2000); doi: 10.1117/12.397860; https://doi.org/10.1117/12.397860
PROCEEDINGS
8 PAGES


SHARE
Back to Top