You have requested a machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Neither SPIE nor the owners and publishers of the content make, and they explicitly disclaim, any express or implied representations or warranties of any kind, including, without limitation, representations and warranties as to the functionality of the translation feature or the accuracy or completeness of the translations.
Translations are not retained in our system. Your use of this feature and the translations is subject to all use restrictions contained in the Terms and Conditions of Use of the SPIE website.
29 November 2000Low-temperature preparation of BaTiO3 thin film by MOD and hydrothermal treatment
PbTiO3 (PT) thin film with perovskite-type microstructure was synthesized directly on transparent sapphire using a rf-magnetron sputtering system with a composite target. The results show that the film is completely [111] oriented, and the lattice constant is larger than that of bulk PT material. The optical properties were calculated from the transmittance spectrum alone, and the dispersion was found to fit the single-term Sellmeier relation well. The minimum refractive index of the film is found to be 2.51, and the direct band-gap energy is estimated to be 3.65 eV from the linear fitting of the absorption coefficient to the Tauc plot of ((alpha) hv)2 vs hv.
The alert did not successfully save. Please try again later.
Quingchun Zhao, Zhengxiu Fan, Zhaosheng Tang, Jian-Da Shao, "Microstructure and optical properties of PbTiO3 film deposited on transparent sapphire by rf sputtering," Proc. SPIE 4086, Fourth International Conference on Thin Film Physics and Applications, (29 November 2000); https://doi.org/10.1117/12.408344