2 November 2000 Laser treatment of the 38HMJ steel surface in a liquid nitrogen environment
Author Affiliations +
Abstract
Samples of the 38HMJ steel kept in a liquid nitrogen bath (LN2) at 77 K are treated by a 1 kW CO2 laser beam of intensity of about 1.3x105W/cm2 on the sample surface. For thermal processing by means of the 10,6 micrometers radiation the transparency window of LN2 below 0.3 eV is utilised. The irradiation effects are compared with results obtained for the reference samples of the same material under standard gas shielding conditions. Measurements of microhardness HV 0.1 indicated on reduction of the heat affected zone for the LN2 case. A similar effect is observed for higher sample velocities and a value of about 700 HV is obtained in a 30 micrometers surface layer. Surface analysis by means of Auger electron spectroscopy confirms the local nitrogen element of the laser treated areas depending on the processing conditions.
© (2000) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Rafal Jendrzejewski, Rafal Jendrzejewski, Gerard Sliwinski, Gerard Sliwinski, Ilia Martev, Ilia Martev, Nikolay N. Nedialkov, Nikolay N. Nedialkov, Peter A. Atanasov, Peter A. Atanasov, } "Laser treatment of the 38HMJ steel surface in a liquid nitrogen environment", Proc. SPIE 4238, Laser Technology VI: Applications, (2 November 2000); doi: 10.1117/12.405970; https://doi.org/10.1117/12.405970
PROCEEDINGS
6 PAGES


SHARE
RELATED CONTENT

Laser processing of slate tiles
Proceedings of SPIE (August 13 2001)
Laser selectivity on cleaning museologic iron artefacts
Proceedings of SPIE (April 25 2007)
Selected aspect of diffusion initiated by a laser beam
Proceedings of SPIE (February 28 1995)
Laser Heat Treatment Of Iron-Base Alloys
Proceedings of SPIE (September 29 1985)
Effect of a CO2 laser treatment of steel surface at...
Proceedings of SPIE (October 02 1997)

Back to Top