9 July 2001 Effect of osmolarity on shape retention following laser-mediated cartilage reshaping
Author Affiliations +
Proceedings Volume 4257, Laser-Tissue Interaction XII: Photochemical, Photothermal, and Photomechanical; (2001) https://doi.org/10.1117/12.434704
Event: BiOS 2001 The International Symposium on Biomedical Optics, 2001, San Jose, CA, United States
Abstract
Laser reshaping of mechanically deformed cartilage specimens accelerates stress relaxation and results in permanent shape change. The mechanism of laser-mediated cartilage reshaping is still unknown, but clearly depends upon the complex molecular interactions between the physio-chemical environment and matrix proteins (collagen, and proteoglycans). It is well known in articular tissues that the mechanical properties of cartilage are sensitive to changes in tissue pH and osmolarity. The objective of this study was to determine the effect of osmolarity on shape change during laser reshaping in morphologic cartilage tissues. Porcine nasal septal cartilage specimens were cut (20 x 5 x 1.5 mm) and immersed in osmotically graded NaCl (0.2NS, 0.8NS, 1.0NS, 1.2 NS and 5 NS) or Phosphate buffered (0.2NS, 0.9NS, 1.0NS, 1.1NS, and 5NS) solutions for 12 hours to establish equilibrium. Then, specimens were bent into semicircular shapes, secured with clamps, and irradiated with an Nd:YAG laser (λ= 1320nm, 5W, 15 secs, 5 mm spot size) along the region of maximum curvature. Resultant bend angle was measured. Shape retention was calculated by comparing resultant curvature with pre-irradiation measurements. Non-irradiated, untreated (negative controls) cartilage retained less than 46% of the original bend. There was no difference in shape retention with respect to varying osmolarity (changed tissue water content) in either group. Resultant bend angles varied from 84 degree(s) to 194 degree(s) corresponding to shape retention varying from 42% to 72% in specimens which were immersed in either NaCl of Phosphate buffered solutions. While laser heating of deformed specimens does result in significant reshaping, the alterations in osmolarity do not seem to effect this process significantly over the range of values evaluated in this study.
© (2001) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Amir M. Karamzadeh, Amir M. Karamzadeh, Darren S. Gray, Darren S. Gray, Joey Ann Kimball, Joey Ann Kimball, Brian Jet-Fei Wong, Brian Jet-Fei Wong, } "Effect of osmolarity on shape retention following laser-mediated cartilage reshaping", Proc. SPIE 4257, Laser-Tissue Interaction XII: Photochemical, Photothermal, and Photomechanical, (9 July 2001); doi: 10.1117/12.434704; https://doi.org/10.1117/12.434704
PROCEEDINGS
9 PAGES


SHARE
Back to Top