Defect generation in fused silica under high-intensity laser interaction

Andrejs Silins

doi:10.1117/12.425073

12 April 2001 Defect generation in fused silica under high-intensity laser interaction

Andrejs Silins

Proceedings Volume 4347, Laser-Induced Damage in Optical Materials: 2000; (2001) https://doi.org/10.1117/12.425073
Event: Laser-Induced Damage in Optical Materials: 2000, 2000, Boulder, CO, United States

Abstract

Interaction of high intensity laser radiation with fused silica mainly introduces strong temperature increase in the region where this radiation is absorbed. The local temperature rises up to 2500 K or higher. At these temperatures high concentrations of thermal intrinsic point defects are generated. Estimated concentrations of equilibrium oxygen excess defects at 2500 K reaches 7(DOT)10¹⁸cm^-3 and the main part of these defects are non-bridging oxygen atoms. Before equilibrium large part of oxygen excess defects are oxygen molecules. Presence of oxygen molecules in concentration 3(DOT)10¹⁸cm^-3 creates the local internal pressure 1,0 atm. at 2500 K. As the result the boiling and evaporation of the material from the region where high intensity laser radiation is absorbed occurs. Remaining material contains increased concentrations of oxygen deficit point defects, such as three- and two-fold coordinated silicon atoms, as well as oxygen excess point defects which are tightly bonded to the glass network, such as non- bridging oxygen atoms. Presence of these defects causes the strong increase of UV-wavelength laser radiation absorption. This stimulates additional laser interaction with fused silica. New features in defect generation appears when very short (femtosecond) laser pulses are used. In this case the laser pulse length is comparable with the period of main atomic vibrations in fused silica. Such conditions open new sub-threshold intrinsic defect generation mechanisms.

Citation Download Citation

Andrejs Silins "Defect generation in fused silica under high-intensity laser interaction", Proc. SPIE 4347, Laser-Induced Damage in Optical Materials: 2000, (12 April 2001); https://doi.org/10.1117/12.425073

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available