2 November 2001 Infrared absorption of Czochralski germanium and silicon
Author Affiliations +
Abstract
The current report demonstrates the temperature vs. transmission vs. resistivity relationship for the less explored IR wavelength range of 6 to 22 micrometers for silicon and 10 to 22 micrometers for germanium over the temperature range of -100 degrees C to 25 degrees C. These studies involve a wide range of resistivities. Material samples include n- type Si of 4000, 160, and 12 ohm-cm, and n-type Ge of 35, 2.5, and 0.5 ohm-cm. Silicon has useable transmission bands only between 1.2 and 8.5 micrometers , between 14 and 15.6 micrometers , and greater than 20 micrometers with best transmission occurring between 1.2 and 6.5 micrometers . Germanium has a useable transmission band between 2 and 17 micrometers with best transmission between 2 and 11.5 micrometers . The temperature dependence of IR transmission becomes more pronounced with increasing wavelength: 1.5 percent to 11.5 percent and 3 percent to 9.5 percent for silicon and germanium respectively over the temperature range of -100 degrees C to 25 degrees C. The 4000 ohm-cm Si sample exhibits significantly greater transmission at wavelengths of both 9.0 and 19.5 microns. The temperature dependence of lattice absorption is observed in germanium. This study builds a bridge between previously determined absorption mechanisms of the near and far IR ranges and may be used to develop the feasibility of silicon and germanium as optical windows or lenses within an extraterrestrial environment.
© (2001) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Jason E. Peters, Jason E. Peters, P. Darrell Ownby, P. Darrell Ownby, Charles R. Poznich, Charles R. Poznich, Jroy C. Richter, Jroy C. Richter, Dennis W. Thomas, Dennis W. Thomas, } "Infrared absorption of Czochralski germanium and silicon", Proc. SPIE 4452, Inorganic Optical Materials III, (2 November 2001); doi: 10.1117/12.446889; https://doi.org/10.1117/12.446889
PROCEEDINGS
8 PAGES


SHARE
RELATED CONTENT

Far-infrared absorption of Czochralski germanium and silicon
Proceedings of SPIE (September 22 1998)
Transparent Polycrystalline Lanthana-Doped Yttria
Proceedings of SPIE (December 25 1984)
High Temperature IR Absorption Of Low Resistivity Germanium
Proceedings of SPIE (September 10 1989)
Specifications For Optical Grade Germanium And Silicon Blanks
Proceedings of SPIE (December 08 1983)

Back to Top