11 July 2002 Next-generation electroceramic fibers for active control
Author Affiliations +
Abstract
Lead-based PMN-31PT and lead-free BNBZT fibers in the 250- 500 micrometer diameter range were produced using CeraNova's proprietary extrusion technology. Various recrystallization approaches were investigated, including seeded solid state conversion and self-seeded texturing, with the goal of obtaining single-crystalline or textured macrocrystalline fibers. Grains in excess of 100 micrometers - and exceeding 1 mm in some cases - with surface and bulk coverage approaching 100 percent, were obtained in a narrow temperature range and under carefully controlled atmosphere conditions. Large grain growth in BNBZT required the presence of BaSrTiO3 or SrTiO3 seeds and temperatures in the 1150-1200 degrees C range. In PMN-31PT, nearly compete recrystalline was observed in unseeded material at relatively low temperature and short time, and improved performance was achieved with a two-step sintering schedule and slightly extended time. While conduction effects have not yet allowed compete assessment of recrystalline BNBZT, PMN-31PT fibers have shown excellent piezoelectric properties with remanent polarization in excess of 30(mu) C/cm2 and coercive field of 4.5kV/cm. When incorporated into active fiber composites, the latter fibers' performance of 2000 microstrain in superior to average PZT-based production composites. Efforts are under way to induce preferred orientation in the large crystal in order to maximize performance.
© (2002) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Pavel Bystricky, Marina R. Pascucci, Harold B. Strock, "Next-generation electroceramic fibers for active control", Proc. SPIE 4699, Smart Structures and Materials 2002: Active Materials: Behavior and Mechanics, (11 July 2002); doi: 10.1117/12.474971; https://doi.org/10.1117/12.474971
PROCEEDINGS
9 PAGES


SHARE
Back to Top