27 December 2002 Higher Anisotropy and Improved Surface Conditions for 90nm Node MoSiON ICP Dry Etch
Author Affiliations +
Abstract
Embedded-attenuated phase shift masks (EAPSMs) have been an indispensable enabling technology for <130 nm node device fabrication. The precise etching of MoSiON is a key process in high quality phase shift mask manufacturing. Fluorine-based plasma chemistry has been used widely to date, but it is difficult to control CD (Critical Dimension) and phase uniformity. This stems mainly from the large Cr undercut and surface roughness due to the reaction of fluorine radicals with the phase shifting layer. In this paper, etch characteristics of the MoSiON layer using CF4, O2, and He in an inductively coupled plasma (ICP) were examined for the manufacturing of phase shift masks for 90-nm node design rules. The dependency of etch parameters such as ICP power, bias power (DC bias voltage), pressure, CF4 concentration, and O2 concentration on the etch properties of MoSiON were tested. We have investigated vertical slope, surface morphology, and minimum CD bias. This optimized process condition showed that intra-mask phase uniformity was below 1% (3-sigma) over a 135 mm × 135 mm mask area and transmittance uniformity was 8.68% ± 0.09%. CD uniformity was 5.5nm (3-sigma), CD linearity was 5.0nm over 300nm to 1300nm, and Cr-to-MoSiON CD bias was 2.0nm. The MoSiON profile was nearly vertical and the surface morphology was very clean.
© (2002) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Dong-Soo Min, Byung-Soo Chang, Hyuk-Joo Kwon, and Boo-Yeon Choi "Higher Anisotropy and Improved Surface Conditions for 90nm Node MoSiON ICP Dry Etch", Proc. SPIE 4889, 22nd Annual BACUS Symposium on Photomask Technology, (27 December 2002); https://doi.org/10.1117/12.467493
PROCEEDINGS
8 PAGES


SHARE
Advertisement
Advertisement
RELATED CONTENT

Simpler attenuated phase-shifting mask
Proceedings of SPIE (July 05 2000)
Study on the soft defects related to dry etch process...
Proceedings of SPIE (October 13 2011)
Dry etching technology of Cr and MoSi layers using high...
Proceedings of SPIE (January 22 2001)
Actual use of phase-shift mask
Proceedings of SPIE (December 08 1995)

Back to Top