15 January 2003 Embossing of microscale features in Pb and Zn
Author Affiliations +
Proceedings Volume 4979, Micromachining and Microfabrication Process Technology VIII; (2003) https://doi.org/10.1117/12.472758
Event: Micromachining and Microfabrication, 2003, San Jose, CA, United States
Abstract
Embossing of microscale features into Pb and Zn was carried out using LIGA (Lithographie, Galvanoformung, Abformung) fabricated Ni mold inserts with features 100 microns in diameter and 500 microns in height. Molding was carried out at 300 °C with both uncoated Ni inserts and Ni inserts coated with Ti-containing hydrocarbon (Ti-C:H). The coatings were applied using a high-density inductively coupled plasma (ICP) assisted hybrid chemical vapor deposition (CVD)/physical vapor deposition (PVD) technique. This technique is shown to produce coatings conformally onto LIGA fabricated high aspect ratio microstructures (HARMs). The performance of the molding process was characterized using scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy both in terms of the features generated and the insert condition after molding. The present results indicate that in molding metals that are not reactive with Ni no coating is necessary to produce the microfeatures. This study also demonstrates that in molding Zn, where significant metal/insert chemical interactions exist, surface engineering of the mold insert is necessary to obtain satisfactory performance. Conformal deposition of engineered ceramic coatings onto Ni microscale mold inserts is an effective means for achieving micromolding of reactive metals.
© (2003) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Dean J. Guidry, Dean J. Guidry, Dong Mei Cao, Dong Mei Cao, Tao Wang, Tao Wang, Wen Jin Meng, Wen Jin Meng, Kevin W. Kelly, Kevin W. Kelly, } "Embossing of microscale features in Pb and Zn", Proc. SPIE 4979, Micromachining and Microfabrication Process Technology VIII, (15 January 2003); doi: 10.1117/12.472758; https://doi.org/10.1117/12.472758
PROCEEDINGS
9 PAGES


SHARE
RELATED CONTENT


Back to Top