16 January 2003 Monocrystalline Si membranes for pressure sensors fabricated by a novel surface micromachining process using porous silicon
Author Affiliations +
We developed a novel surface micromachining process to fabricate monocrystalline silicon membranes covering a vacuum cavity without any additional sealing steps. Heart of the process is anodic etching of porous silicon, annealing and epitaxial growth. The porous silicon layer consists of two parts, a starting mesoporous silicon layer with low surface porosity and a nanoporous silicon layer with a high porosity. The following annealing step removes native oxide within the later cavity, and the surface is sealed for the subsequent epitaxial layer deposition. The observed stacking fault density in the epitaxial layer about 1E5 cm-2. The temperature budget of the following ASIC-process leads to a complete transformation of the nanoporous silicon layer into a large cavity. The whole structure can be used as a pressure sensor. The estimated pressure in the cavity is smaller than 1 mbar. First integrated pressure sensors have been fabricated using this process. The sensors show a good linearity over the whole pressure range of 200 mbar to 1000 mbar. This novel process has several advantages compared to already published processes. It is a “MEMS first” process, which means that after the epitaxial growth the surface of the wafer is close to a standard wafer surface. Due to full IC compatibility, standard ASIC processes are possible after the fabrication of the membrane. The use of porous silicon enables a high degree of geometrical freedom in the design of membranes compared to standard bulk micromachining (KOH, TMAH). The monocrystalline membranes can be fabricated with surface micromachining without any additional sealing or backside processing steps.
© (2003) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Hans Artmann, Hans Artmann, Frank Schaefer, Frank Schaefer, Gerhard Lammel, Gerhard Lammel, Simon Armbruster, Simon Armbruster, Hubert Benzel, Hubert Benzel, Christoph Schelling, Christoph Schelling, Heribert Weber, Heribert Weber, Heinz-Georg Vossenberg, Heinz-Georg Vossenberg, Ronald Gampp, Ronald Gampp, Joerg Muchow, Joerg Muchow, Franz Laermer, Franz Laermer, Stefan Finkbeiner, Stefan Finkbeiner, } "Monocrystalline Si membranes for pressure sensors fabricated by a novel surface micromachining process using porous silicon", Proc. SPIE 4981, MEMS Components and Applications for Industry, Automobiles, Aerospace, and Communication II, (16 January 2003); doi: 10.1117/12.479564; https://doi.org/10.1117/12.479564


Integration of MEMS devices
Proceedings of SPIE (September 28 1999)
Study of the selectivity of porous silicon formation
Proceedings of SPIE (October 25 1994)
Anisotropic chemical etching of silicon
Proceedings of SPIE (April 15 1998)

Back to Top