Characteristics of solder joints under fatigue loads using piezomechanical actuation

Dong-Jin Shim; S. Mark Spearing

doi:10.1117/12.497949

22 July 2003 Characteristics of solder joints under fatigue loads using piezomechanical actuation

Dong-Jin Shim, S. Mark Spearing

Proceedings Volume 5045, Testing, Reliability, and Application of Micro- and Nano-Material Systems; (2003) https://doi.org/10.1117/12.497949
Event: NDE for Health Monitoring and Diagnostics, 2003, San Diego, California, United States

Abstract

Crack initiation and growth characteristics of solder joints under fatigue loads are investigated using piezomechanical actuation. Cracks in solder joints, which can cause failure in microelectronics components, are induced via piezoelectricity in piezo-ceramic bonded joints. Lead-zirconate-titanate ceramic plates and eutectic Sn-Pb solder bonded in a double-lap shear configuration are used in the investigation. Electric field across each piezo-ceramic plate is applied such that shear stresses/strains are induced in the solder joints. The experiments show that cracks initiate in the solder joints around defects such as voids and grow in length until they coalesce with other cracks from adjacent voids. These observations are compared with the similar thermal cycling tests from the literature to show feasibility and validity of the current method in investigating the fatigue characteristics of solder joints. In some specimens, cracks in the piezo-ceramic plates are observed, and failure in the specimens generally occurred due to piezo-ceramic plate fracture. The issues encountered in implementing this methodology such as low actuation and high processing temperatures are further discussed.

Citation Download Citation

Dong-Jin Shim and S. Mark Spearing "Characteristics of solder joints under fatigue loads using piezomechanical actuation", Proc. SPIE 5045, Testing, Reliability, and Application of Micro- and Nano-Material Systems, (22 July 2003); https://doi.org/10.1117/12.497949

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available