22 July 2003 Microstructural study of nanoprecipitates in RRA treated Al-7075 T6 using AFM/UFM/STEM
Author Affiliations +
Abstract
7075 T651 aluminum alloy is frequently used in aircraft applications for its high strength to weight ratio. However, aircraft parts made of this alloy have been plagued by stress corrosion cracking (SCC). Retrogression and re-aging (RRA) is a post T651 two-stage heat treatment that provides improved SCC resistance with minimal loss in tensile strength. In this study, various forms of microscopy and mechanical testing are used to investigate how the RRA process affects the microstructure. The microscopic observations in this paper show that the precipitates in the aluminum alloy coarsen and that the grain boundary regions are depleted of copper and magnesium. The mechanical testing performed shows that the aluminum alloy decreases in strength and increases in conductivity when exposed to longer retrogression times prior to re-aging.
© (2003) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Samuel J. M. Kuhr, M. F. Pinnell, Daniel Eylon, "Microstructural study of nanoprecipitates in RRA treated Al-7075 T6 using AFM/UFM/STEM", Proc. SPIE 5045, Testing, Reliability, and Application of Micro- and Nano-Material Systems, (22 July 2003); doi: 10.1117/12.484000; https://doi.org/10.1117/12.484000
PROCEEDINGS
12 PAGES


SHARE
RELATED CONTENT


Back to Top