14 October 2003 Compositionally and structurally modulated Pb(Mg1/3Nb2/3)O3-PbTiO3 relaxor thin films for microactuator application
Author Affiliations +
Proceedings Volume 5062, Smart Materials, Structures, and Systems; (2003) https://doi.org/10.1117/12.514576
Event: Smart Materials, Structures, and Systems, 2002, Bangalore, India
Thin films of (1-x)Pb(Mg1/3Nb2/3)O3-xPbTiO3(x = 0.1 to 0.3) (PMN-PT) were successfully grown on the platinum coated silicon substrate by pulsed excimer laser ablation technique. A thin template layer of LaSr0.5Co0.5O3 (LSCO) was deposited on platinum substrate prior to the deposition of PMN-PT thin films. The composition and the structure of the films were modulated via proper variation of the deposition parameter such as substrate temperature, laser fluence and thickness of the template layers. We observed the impact of the thickness of LSCO template layer on the orientation of the films. The crystallographic structure and compositional variation were confirmed with x-ray diffraction and energy diffraction x-ray (EDX) analysis. A room temperature dielectric constant varying from 2000 to 4500 was noted for different composition of the films. The dielectric properties of the films were studied over the frequency range of 100 Hz - 100 kHz over a wide range of temperatures. The films exhibited the relaxor-type behavior that was characterized by the frequency dispersion of the temperature of dielectric constant maxima (Tm) and also diffuse phase transition. This relaxor nature in PMN-PT thin films was attributed to freezing of the dipole moment, which takes place below a certain temperature. This phenomenon was found to be very similar to spin glass system, where spins are observed to freeze after certain temperature.
© (2003) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Apurba Laha, Apurba Laha, Saluru B. Krupanidhi, Saluru B. Krupanidhi, } "Compositionally and structurally modulated Pb(Mg1/3Nb2/3)O3-PbTiO3 relaxor thin films for microactuator application", Proc. SPIE 5062, Smart Materials, Structures, and Systems, (14 October 2003); doi: 10.1117/12.514576; https://doi.org/10.1117/12.514576

Back to Top