Large area sapphire windows have been fabricated by edge-bonding multiple panes. A 4-pane edge-bonded 320 x 410 x 7 mm sapphire window with excellent optical characteristics has been successfully finished. Two different bonding methods were used to build up the 4-pane window blank. Pairs of commercially available EFG sapphire panes were first bonded using a 1500°C bonding process. The bonded pairs were then joined using a 1100°C process. Bond strengths for the two methods are approximately 130 MPa (20 kpsi). Optical finishing was completed using standard methods for sapphire with no significant increase in finishing time caused by the bonds. There are no deleterious optical effects or visible optical distortion due to the bond lines. The edge bonding technology can now produce 600 x 600 mm flat window blanks. Conformal windows have also been produced using the edge bonding method. Very high bond strengths of 250 MPa (37 kpsi) have been attained on smaller samples using an optimized solid ceramic fillet.
© (2003) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Richard L. Gentilman, Patrick Timothy McGuire, Daniel Fiore, Kim Ostreicher, Joel Askinazi, "Large-area sapphire windows", Proc. SPIE 5078, Window and Dome Technologies VIII, (26 September 2003); doi: 10.1117/12.501435; https://doi.org/10.1117/12.501435
PROCEEDINGS
7 PAGES


SHARE
KEYWORDS
Sapphire

Ceramics

Crystals

Solids

Zinc

Polishing

Distortion

RELATED CONTENT

Advancements in MWIR window materials and structures
Proceedings of SPIE (June 06 2013)
Recent advances in ALON optical ceramic
Proceedings of SPIE (May 18 2005)
Producing large EFG© sapphire sheet for VIS IR (500 5000...
Proceedings of SPIE (October 15 2005)
Large-area edge-bonded flat and curved sapphire windows
Proceedings of SPIE (September 07 2001)
Large-area flat and curved sapphire window blanks
Proceedings of SPIE (October 25 2000)
High-strength edge-bonded sapphire windows
Proceedings of SPIE (July 26 1999)

Back to Top