You have requested a machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Neither SPIE nor the owners and publishers of the content make, and they explicitly disclaim, any express or implied representations or warranties of any kind, including, without limitation, representations and warranties as to the functionality of the translation feature or the accuracy or completeness of the translations.
Translations are not retained in our system. Your use of this feature and the translations is subject to all use restrictions contained in the Terms and Conditions of Use of the SPIE website.
28 May 2003Electron-beam mask repair with induced reactions
Electron-beam induced chemical reactions and their applicability to mask repair are investigated. For deposition and chemical etching with a focused electron-beam system, it is required to disperse chemicals in a molecular beam to the area of interest with a well-defined amount of molecules and monolayers per second. For repair of opaque defects the precursor gas reacts with the absorber material of the mask and forms a volatile reaction product, which leaves the surface. In this way the surface atoms are removed layer by layer. For clear defect repair, additional material, which is light absorbing in the UV, is deposited onto the defect area. This material is rendered as a nanocrystalline deposit from metal containing precursors. An experimental electron-beam mask repair system is developed and used to perform exploratory work applicable to photo mask, EUV mask, EPL and LEEPL stencil mask repair. The tool is described and specific repair actions are demonstrated. Platinum deposited features with lateral dimensions down to 20 nm demonstrate the high resolution obtainable with electron beam induced processes, while AFM and AIMS measurements indicate, that specifications for mask repair at the 70 nm device node can be met. In addition, examples of etching quartz, TaN, and silicon carbide stencil masks are given.
The alert did not successfully save. Please try again later.
Hans W. P. Koops, Klaus Edinger, Johannes Bihr, Volker A. Boegli, Jens Greiser, "Electron-beam mask repair with induced reactions," Proc. SPIE 5148, 19th European Conference on Mask Technology for Integrated Circuits and Microcomponents, (28 May 2003); https://doi.org/10.1117/12.514972