6 February 2004 Enhanced photovoltaic efficiency in polymer-fullerene composites by thermally controlled interdiffusion
Author Affiliations +
Proceedings Volume 5215, Organic Photovoltaics IV; (2004); doi: 10.1117/12.506586
Event: Optical Science and Technology, SPIE's 48th Annual Meeting, 2003, San Diego, California, United States
Abstract
The interface between polymer and fullerene in organic photovoltaic devices is improved by thermally induced interdiffusion. Starting from a bilayer of 2-methoxy-5-(2’-ethylhexyloxy)-1,4-phenylenevinylene copolymer (MEH-PPV) and the Buckminsterfullerene (C60) devices are heated in the vicinity of the glass transition temperature creating a gradient bulk-heterojunction. Interdiffused devices show photoluminescence quenching with concomitant improvements in photocurrents. Variation of the polymer layer thickness shows an increase in photocurrents with decreasing layer thickness within the examined thickness regime as transport of the separated charges out of the device is improved. The interdiffusion was observed in situ by monitoring the photocurrents during the heating step. Cross-sectional transmission electron microscopy reveals C60 clusters of up to 30 nm in diameter in the interdiffused devices. The clustering of the fullerene molecules puts a significant constraint on the interdiffusion process.
© (2004) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Martin Drees, James Randolph Heflin, Richey Davis, Daniela Topasna, Paige Stevenson, "Enhanced photovoltaic efficiency in polymer-fullerene composites by thermally controlled interdiffusion", Proc. SPIE 5215, Organic Photovoltaics IV, (6 February 2004); doi: 10.1117/12.506586; https://doi.org/10.1117/12.506586
PROCEEDINGS
10 PAGES


SHARE
KEYWORDS
Polymers

Transmission electron microscopy

Fullerenes

External quantum efficiency

Absorption

Interfaces

Luminescence

Back to Top