25 February 2004 Multiple pulses laser irradiation study in silica
Author Affiliations +
Abstract
Cumulative laser irradiations are performed on silica at 1064nm and 355nm with a 7ns pulsed laser. The experiments are made in bulk and surface of materials thanks to a focused beam (12μm and 8μm respectively for each wavelength). The small beam size combined to a reliable statistical measurement of laser damage, allow us to plot accurate laser damage probability curves. Moreover the use of an adapted statistic model permit to deduce from these curves the laser damage precursor centers densities. These nano-sized precursors are established by different works to be responsive of the breakdown initiation. In a previous work realized at 1064nm, we have observed in our specific conditions, that multiple irradiation leads clearly to a decrease of the laser damage threshold. Furthermore we have highlighted that at this wavelength, the precursor densities were invariant with the number of shot. These results had given novel information about the damage initiation process. Indeed the same precursor centers seems to be involved in the initiation process in spite of the decrease of they laser damage threshold whatever the number of shot. In this paper we will shown new results obtained at 355nm in silica with the same measurement process. The case of silica surface is also examined for the two wavelengths. The experimental data exhibit a strong different behavior, regarding the precursor densities evolution versus the number of shot.
© (2004) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Jean-Yves Natoli, Jean-Yves Natoli, Bertrand Bertussi, Bertrand Bertussi, Laurent Gallais, Laurent Gallais, Mireille Commandre, Mireille Commandre, Claude Amra, Claude Amra, } "Multiple pulses laser irradiation study in silica", Proc. SPIE 5250, Advances in Optical Thin Films, (25 February 2004); doi: 10.1117/12.513377; https://doi.org/10.1117/12.513377
PROCEEDINGS
6 PAGES


SHARE
Back to Top