14 June 2004 Er3+/Yb3+-codoped soda-lime silicate glasses: a case study
Author Affiliations +
Abstract
Silicate glasses are among the best hosts for rare-earth ions, especially for the development of integrated optic amplifiers and lasers, due to their chemical robustness and adaptability to different waveguide fabrication processes. We performed a detailed study of a set of six experimental soda-lime silicate glasses, all having approximately the same base composition but doped with different percentages of Er3+ and Yb3+ ions. Judd-Ofelt analysis was performed on these glasses and the calculated radiative lifetimes were compared with the experimental ones. Planar waveguides were fabricated by using ion-exchange technology, and a new analytical function was used to fit the index profile of the waveguides. Luminescence and Raman spectroscopy was performed on most waveguide samples, and upconversion emission was evaluated. Channel waveguide insertion losses were reduced by using annealing processes, and net gain around 1535 nm was obtained. The gain, so far, is limited, but we are confident to be able to further increase the amplifier performances. Meanwhile, we are also developing a new type of silicate glass doped with alumina in order to increase the gain bandwidth.
© (2004) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Simone Berneschi, Marco Bettinelli, Massimo Brenci, Roberto Calzolai, Alessandro Chiasera, Maurizio Ferrari, Gualtiero Nunzi Conti, Stefano Pelli, Sergio Sebastiani, Adolfo Speghini, Jie Zheng, and Giancarlo C. Righini "Er3+/Yb3+-codoped soda-lime silicate glasses: a case study", Proc. SPIE 5350, Optical Components and Materials, (14 June 2004); https://doi.org/10.1117/12.530423
PROCEEDINGS
7 PAGES


SHARE
Advertisement
Advertisement
RELATED CONTENT


Back to Top