20 May 2004 Plasticizer-assisted polymer imprint and transfer
Author Affiliations +
Abstract
We have developed a new method to pattern polymeric materials, including non-thermoplastic polymers, at low temperature and low pressure. In this method, plasticizers are added to increase the chain mobility of the polymers, resulting in lower imprinting temperature and/or pressure. Two established imprinting and transfer techniques were chosen to demonstrate this method, namely, conventional nanoimprint lithography (NIL) and microcontact printing (μCP). These two techniques were used to pattern poly(3,4-ethylenedioxythiophene) (PEDOT). PEDOT was chosen because it is a non-thermoplastic polymer and therefore cannot be easily patterned using conventional NIL. Successful imprint of PEDOT films from the PDMS mold was achieved at a low pressure of 10 kPa and 25°C by controlled addition of glycerol as a plasticizer using conventional NIL; well-defined arrays of 2μm wide, 185 nm high PEDOT dots have also been demonstrated by μCP. In contrast, patterning of PEDOT film without plasticizer requires higher temperature (80°C) and pressure (10 MPa), which could cause severe deformation of the transferred patterns. This method of plasticizer-assisted imprint lithography (PAIL) broadens the applicapability of NIL to a wide range of polymeric materials.
© (2004) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Li Tan, Li Tan, Yen Peng Kong, Yen Peng Kong, Stella W. Pang, Stella W. Pang, Albert F. Yee, Albert F. Yee, } "Plasticizer-assisted polymer imprint and transfer", Proc. SPIE 5374, Emerging Lithographic Technologies VIII, (20 May 2004); doi: 10.1117/12.534290; https://doi.org/10.1117/12.534290
PROCEEDINGS
6 PAGES


SHARE
Back to Top